Asphalt Emulsion is dark-brown liquid made of asphalt finely dispersed in water, to be sprayed over road layer or mixed with aggregate in atmospheric temperature.
Delivery is made either by distributor(sprayer) vehicles or drums(200lit./18lit.).
|Product Name||Applied Standard||Outline/Application||Leaflet|
|PK-1,2||JIS K 2208 PK-1,2||Kationic emulsion for penetration. Used for surface treatment by penetration, chip-seal, SAMI-method.|
|PK-3||JIS K 2208 PK-3||Kationic emulsion for penetration. Used for prime-coat.|
|PK-4||JIS K 2208 PK-4||Kationic emulsion for penetration. Used for tack-coat.|
|MK-1〜3||JIS K 2208 MK-1〜3||Kationic emulsion for mixing. Used for cold mixing (stabilizer/plant-mix method), on-site surface recycle method, slurry-seal method, fog-seal method.||−|
|Ceme-Set||JIS K 2208 MN-1||Designed to mix with cement. Used for in-place CAE base recycle method.|
|Penetor-E||JEAAS PK-P*||High-penetrative kationic emulsion. Higher-penetration than PK-3.|
|High-Tack||JEAAS PK-H*||High-density (>65% asphalt content) kationic emulsion. Quicker resolution and greater tenacity than PK-1,2. Used for penetration surface treatment, chip-seal, SAMI-method.|
|Premi-Set||JEAAS MK-C*||Emulsion for mixing containing cut-back asphalt. Usable even after resolution, for cold mixture (plant-mix), OGEM-method.||−|
|PKR-T||JEAAS PKR-T*||Rubberized emulsion. Stronger binding effect than PK-4. Used for tack-coat (mainly of porous pavement).|
|PKR-S(-1,-2)||JEAAS PKR-S-1,2*||Rubberized emulsion. Stronger binding effect than PK-1,2. Used for surface treatment, chip-seal, SAMI-method.|
|Poly-Seal||JEAAS MS-1*||Modified asphalt emulsion. High tenacity & quick resolution. Used for micro-surfacing.||−|
|JEAAS PKM-T*||Modified asphalt emulsion. Forms firmer and less sticky tack coat surface after resolution. Used to create anti-adhesion property (to vehicle tires).|
|N/A||Modified asphalt emulsion. Penetrates into existing cracks to form thicker tack coat surface. Used for SHOREKI-unique reflection-crack prevention.
|Asmo-Tack||N/A||Rubberized/modified emulsion. Higher density than PKR-S, higher modified for larger tenacity. Used for surface treatment, chip-seal, SAMI-method.||−|
|GMK-8||Rubberized emulsion for mixing. Forms firmer/stiffer film after resolution.||−|
|Mor-Foam||Nonionic emulsion for mixing. Good compatibility with cement. Solidifies smoky dust, forms water-proof layer.||−|
|Clear-Set||Clear emulsion for mixing. High clearness after resolution. Used for wood-chip pavement, colored micro-surfacing, cold clear pavement.||−|
*JEAAS: Japan Emulsified Asphalt Association Standard